| Property |
Ti-15V-3Cr-3Sn-3Al STA sheet, <=1.9 mm (MIL-HDBK-5H)
Ti-15V-3Cr-3Sn-3Al; solution treated and aged; sheet; <=1.9 mm | sheet
|
|---|---|
| Density |
4761 kg/m^3
Density
Historical Nominal
Ti-15V-3Cr-3Sn-3Al; solution treated and aged; sheet; <=1.9 mm; S-basis, <=0.125 in STA 1000 degF/8 h column
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Shear modulus |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Poisson's ratio |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Yield strength |
965.266 MPa
Tensile yield strength, L
Historical Public Release Table Value
Ti-15V-3Cr-3Sn-3Al; solution treated and aged; sheet; <=1.9 mm; S-basis, <=0.125 in STA 1000 degF/8 h column; L direction
965.266 MPa
Tensile yield strength, LT
Historical Public Release Table Value
Ti-15V-3Cr-3Sn-3Al; solution treated and aged; sheet; <=1.9 mm; S-basis, <=0.125 in STA 1000 degF/8 h column; LT direction
958.371 MPa
Compressive yield strength, L
Historical Public Release Table Value
Ti-15V-3Cr-3Sn-3Al; solution treated and aged; sheet; <=1.9 mm; S-basis, <=0.125 in STA 1000 degF/8 h column; L direction
992.845 MPa
Compressive yield strength, LT
Historical Public Release Table Value
Ti-15V-3Cr-3Sn-3Al; solution treated and aged; sheet; <=1.9 mm; S-basis, <=0.125 in STA 1000 degF/8 h column; LT direction
|
| Tensile strength |
999.74 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
Ti-15V-3Cr-3Sn-3Al; solution treated and aged; sheet; <=1.9 mm; S-basis, <=0.125 in STA 1000 degF/8 h column; L direction
999.74 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
Ti-15V-3Cr-3Sn-3Al; solution treated and aged; sheet; <=1.9 mm; S-basis, <=0.125 in STA 1000 degF/8 h column; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|