Metal
Ti-15V-3Cr-3Sn-3Al STA sheet, <=1.9 mm (MIL-HDBK-5H)
Historical public-release S-basis STA sheet reference through 1.9 mm.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 4761 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 999.74 | MPa |
| Tensile yield strength, L | 965.266 | MPa |
| Ultimate tensile strength, LT | 999.74 | MPa |
| Tensile yield strength, LT | 965.266 | MPa |
| Compressive yield strength, L | 958.371 | MPa |
| Compressive yield strength, LT | 992.845 | MPa |
| Ultimate shear strength | 634.318 | MPa |
| Elongation, L | 7 | % |
| Elongation, LT | 7 | % |
| Young's modulus, L | 104.8 | GPa |
| Young's modulus, LT | 108.248 | GPa |
| Compression modulus, L | 105.49 | GPa |
| Compression modulus, LT | 110.316 | GPa |
Units
Condition
- Condition
- Ti-15V-3Cr-3Sn-3Al; solution treated and aged; sheet; <=1.9 mm
- Temper
- STA (1000 degF/8 h)
- Heat treatment
- solution treated and aged 8 hours at 1000 degF per the source table
- Product form
- sheet
- Thickness / diameter range
- <=0.0748 in (1.9 mm), subset of the <=0.125 in table column
- Test direction
- L and LT
- Processing route
- wrought beta titanium-alloy sheet
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.