| Property |
Ti-6Al-2Sn-4Zr-2Mo duplex-annealed sheet, <=2.2 mm (MIL-HDBK-5H)
Ti-6Al-2Sn-4Zr-2Mo; duplex annealed; sheet; <=2.2 mm | sheet
|
|---|---|
| Density |
4540 kg/m^3
Density
Historical Nominal
Ti-6Al-2Sn-4Zr-2Mo; duplex annealed; sheet; <=2.2 mm; A-basis; S-basis elongation; <=0.093 in table columns
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
113.763 GPa
Young's modulus
Historical Nominal
Ti-6Al-2Sn-4Zr-2Mo; duplex annealed; sheet; <=2.2 mm; A-basis; S-basis elongation; <=0.093 in table columns
|
| Shear modulus |
42.747 GPa
Shear modulus
Historical Nominal
Ti-6Al-2Sn-4Zr-2Mo; duplex annealed; sheet; <=2.2 mm; A-basis; S-basis elongation; <=0.093 in table columns
|
| Poisson's ratio |
0.32 -
Poisson's ratio
Historical Nominal
Ti-6Al-2Sn-4Zr-2Mo; duplex annealed; sheet; <=2.2 mm; A-basis; S-basis elongation; <=0.093 in table columns
|
| Yield strength |
861.845 MPa
Tensile yield strength, L
Historical Public Release Table Value
Ti-6Al-2Sn-4Zr-2Mo; duplex annealed; sheet; <=2.2 mm; A-basis; S-basis elongation; <=0.093 in table columns; L direction
861.845 MPa
Tensile yield strength, LT
Historical Public Release Table Value
Ti-6Al-2Sn-4Zr-2Mo; duplex annealed; sheet; <=2.2 mm; A-basis; S-basis elongation; <=0.093 in table columns; LT direction
910.108 MPa
Compressive yield strength, L
Historical Public Release Table Value
Ti-6Al-2Sn-4Zr-2Mo; duplex annealed; sheet; <=2.2 mm; A-basis; S-basis elongation; <=0.093 in table columns; L direction
910.108 MPa
Compressive yield strength, LT
Historical Public Release Table Value
Ti-6Al-2Sn-4Zr-2Mo; duplex annealed; sheet; <=2.2 mm; A-basis; S-basis elongation; <=0.093 in table columns; LT direction
|
| Tensile strength |
930.792 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
Ti-6Al-2Sn-4Zr-2Mo; duplex annealed; sheet; <=2.2 mm; A-basis; S-basis elongation; <=0.093 in table columns; L direction
930.792 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
Ti-6Al-2Sn-4Zr-2Mo; duplex annealed; sheet; <=2.2 mm; A-basis; S-basis elongation; <=0.093 in table columns; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|