Metal
Ti-6Al-2Sn-4Zr-2Mo duplex-annealed sheet, <=2.2 mm (MIL-HDBK-5H)
Historical public-release A-basis duplex-annealed sheet reference through 2.2 mm.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 4540 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 930.792 | MPa |
| Tensile yield strength, L | 861.845 | MPa |
| Ultimate tensile strength, LT | 930.792 | MPa |
| Tensile yield strength, LT | 861.845 | MPa |
| Compressive yield strength, L | 910.108 | MPa |
| Compressive yield strength, LT | 910.108 | MPa |
| Elongation, L | 8 | % |
| Elongation, LT | 8 | % |
| Young's modulus | 113.763 | GPa |
| Compression modulus | 124.106 | GPa |
| Shear modulus | 42.747 | GPa |
| Poisson's ratio | 0.32 | - |
Units
Condition
- Condition
- Ti-6Al-2Sn-4Zr-2Mo; duplex annealed; sheet; <=2.2 mm
- Temper
- duplex annealed
- Heat treatment
- duplex anneal per AMS 4919 and handbook section 5.3.3
- Product form
- sheet
- Thickness / diameter range
- <=0.0866 in (2.2 mm), within the <=0.093 in table columns
- Test direction
- L and LT
- Processing route
- wrought alpha-beta titanium-alloy sheet
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI