| Property |
Ti-6Al-4V solution-treated-and-aged sheet/plate, <=6.3 mm (MIL-HDBK-5H)
Ti-6Al-4V; solution treated and aged; sheet, strip or plate; <=6.3 mm | sheet, strip or plate
|
|---|---|
| Density |
4429 kg/m^3
Density
Historical Nominal
Ti-6Al-4V; solution treated and aged; sheet, strip or plate; <=6.3 mm; S-basis lower value across <=0.1875 and 0.1875-0.750 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
110.316 GPa
Young's modulus
Historical Nominal
Ti-6Al-4V; solution treated and aged; sheet, strip or plate; <=6.3 mm; S-basis lower value across <=0.1875 and 0.1875-0.750 in
|
| Shear modulus |
42.747 GPa
Shear modulus
Historical Nominal
Ti-6Al-4V; solution treated and aged; sheet, strip or plate; <=6.3 mm; S-basis lower value across <=0.1875 and 0.1875-0.750 in
|
| Poisson's ratio |
0.31 -
Poisson's ratio
Historical Nominal
Ti-6Al-4V; solution treated and aged; sheet, strip or plate; <=6.3 mm; S-basis lower value across <=0.1875 and 0.1875-0.750 in
|
| Yield strength |
999.74 MPa
Tensile yield strength, L
Historical Public Release Table Value
Ti-6Al-4V; solution treated and aged; sheet, strip or plate; <=6.3 mm; S-basis lower value across <=0.1875 and 0.1875-0.750 in; L direction
999.74 MPa
Tensile yield strength, LT
Historical Public Release Table Value
Ti-6Al-4V; solution treated and aged; sheet, strip or plate; <=6.3 mm; S-basis lower value across <=0.1875 and 0.1875-0.750 in; LT direction
1034.214 MPa
Compressive yield strength, L
Historical Public Release Table Value
Ti-6Al-4V; solution treated and aged; sheet, strip or plate; <=6.3 mm; S-basis lower value across <=0.1875 and 0.1875-0.750 in; L direction
|
| Tensile strength |
1103.161 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
Ti-6Al-4V; solution treated and aged; sheet, strip or plate; <=6.3 mm; S-basis lower value across <=0.1875 and 0.1875-0.750 in; L direction
1103.161 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
Ti-6Al-4V; solution treated and aged; sheet, strip or plate; <=6.3 mm; S-basis lower value across <=0.1875 and 0.1875-0.750 in; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|