Metal
Ti-6Al-4V solution-treated-and-aged sheet/plate, <=6.3 mm (MIL-HDBK-5H)
Historical public-release S-basis solution-treated-and-aged sheet/plate reference through 6.3 mm.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 4429 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 1103.161 | MPa |
| Tensile yield strength, L | 999.74 | MPa |
| Ultimate tensile strength, LT | 1103.161 | MPa |
| Tensile yield strength, LT | 999.74 | MPa |
| Compressive yield strength, L | 1034.214 | MPa |
| Ultimate shear strength | 641.212 | MPa |
| Elongation, L | 3 | % |
| Elongation, LT | 3 | % |
| Young's modulus | 110.316 | GPa |
| Compression modulus | 113.074 | GPa |
| Shear modulus | 42.747 | GPa |
| Poisson's ratio | 0.31 | - |
Units
Condition
- Condition
- Ti-6Al-4V; solution treated and aged; sheet, strip or plate; <=6.3 mm
- Temper
- solution treated and aged
- Heat treatment
- solution treated and aged per MIL-T-9046 Composition AB-1
- Product form
- sheet, strip or plate
- Thickness / diameter range
- <=0.248 in (6.3 mm), within the <=0.750 in table columns
- Test direction
- L and LT where a value is available across the complete public scope
- Processing route
- wrought alpha-beta titanium-alloy sheet or plate
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI