Materials
Compare Materials
Compare candidate materials with unit-aware values and condition metadata.
| Property |
Ti-6Al-6V-2Sn annealed extrusion, <=101.6 mm (MIL-HDBK-5H)
Ti-6Al-6V-2Sn; annealed; extruded bar or shape; <=101.6 mm | extruded bar or shape
|
|---|---|
| Density |
4540 kg/m^3
Density
Historical Nominal
Ti-6Al-6V-2Sn; annealed; extruded bar or shape; <=101.6 mm; lower A/S-basis value across <=4.000 in
|
| Thermal conductivity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Specific heat capacity |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Young's modulus |
110.316 GPa
Young's modulus
Historical Nominal
Ti-6Al-6V-2Sn; annealed; extruded bar or shape; <=101.6 mm; lower A/S-basis value across <=4.000 in
|
| Shear modulus |
42.747 GPa
Shear modulus
Historical Nominal
Ti-6Al-6V-2Sn; annealed; extruded bar or shape; <=101.6 mm; lower A/S-basis value across <=4.000 in
|
| Poisson's ratio |
0.31 -
Poisson's ratio
Historical Nominal
Ti-6Al-6V-2Sn; annealed; extruded bar or shape; <=101.6 mm; lower A/S-basis value across <=4.000 in
|
| Yield strength |
889.424 MPa
Tensile yield strength, L
Historical Public Release Table Value
Ti-6Al-6V-2Sn; annealed; extruded bar or shape; <=101.6 mm; lower A/S-basis value across <=4.000 in; L direction
882.529 MPa
Tensile yield strength, LT
Historical Public Release Table Value
Ti-6Al-6V-2Sn; annealed; extruded bar or shape; <=101.6 mm; lower A/S-basis value across <=4.000 in; LT direction
930.792 MPa
Compressive yield strength, L
Historical Public Release Table Value
Ti-6Al-6V-2Sn; annealed; extruded bar or shape; <=101.6 mm; lower A/S-basis value across <=4.000 in; L direction
930.792 MPa
Compressive yield strength, LT
Historical Public Release Table Value
Ti-6Al-6V-2Sn; annealed; extruded bar or shape; <=101.6 mm; lower A/S-basis value across <=4.000 in; LT direction
|
| Tensile strength |
965.266 MPa
Ultimate tensile strength, L
Historical Public Release Table Value
Ti-6Al-6V-2Sn; annealed; extruded bar or shape; <=101.6 mm; lower A/S-basis value across <=4.000 in; L direction
965.266 MPa
Ultimate tensile strength, LT
Historical Public Release Table Value
Ti-6Al-6V-2Sn; annealed; extruded bar or shape; <=101.6 mm; lower A/S-basis value across <=4.000 in; LT direction
|
| Elongation at break |
Not listed
Not listed for this material record, condition, or selected unit system.
|
| Maximum service temperature |
Not listed
Not listed for this material record, condition, or selected unit system.
|