Metal
Ti-6Al-6V-2Sn annealed extrusion, <=101.6 mm (MIL-HDBK-5H)
Historical public-release annealed extruded-bar-and-shape reference.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 4540 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 965.266 | MPa |
| Tensile yield strength, L | 889.424 | MPa |
| Ultimate tensile strength, LT | 965.266 | MPa |
| Tensile yield strength, LT | 882.529 | MPa |
| Compressive yield strength, L | 930.792 | MPa |
| Compressive yield strength, LT | 930.792 | MPa |
| Ultimate shear strength | 641.212 | MPa |
| Elongation, L | 10 | % |
| Elongation, LT | 8 | % |
| Ramberg-Osgood exponent, compression L | 26 | - |
| Ramberg-Osgood exponent, tension L | 30 | - |
| Young's modulus | 110.316 | GPa |
| Compression modulus | 113.074 | GPa |
| Shear modulus | 42.747 | GPa |
| Poisson's ratio | 0.31 | - |
Units
Condition
- Condition
- Ti-6Al-6V-2Sn; annealed; extruded bar or shape; <=101.6 mm
- Temper
- annealed
- Heat treatment
- annealed per MIL-T-81556 Composition AB-3
- Product form
- extruded bar or shape
- Thickness / diameter range
- <=4.000 in (101.6 mm)
- Test direction
- L and LT; lower listed value across applicable columns
- Processing route
- wrought alpha-beta titanium-alloy extrusion
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI