Metal
AA3105 base sheet, 6 mm feed, tensile comparison (CC BY experimental)
Measured strength, elongation and exact chemistry for AA3105 base material from a CC BY study.
Properties
Mechanical
| Property | Value | Unit |
|---|---|---|
| Tensile yield strength | 93.9 | MPa |
| Ultimate tensile strength | 132.04 | MPa |
| Elongation | 14.5 | % |
Composition
| Property | Value | Unit |
|---|---|---|
| Silicon mass fraction | 0.23 | % |
| Iron mass fraction | 0.45 | % |
| Copper mass fraction | 0.11 | % |
| Manganese mass fraction | 0.51 | % |
| Magnesium mass fraction | 0.7 | % |
| Titanium mass fraction | 0.05 | % |
| Chromium mass fraction | 0.006 | % |
| Zinc mass fraction | 0.01 | % |
Units
Condition
- Condition
- AA3105 base material used as the tensile comparison in the direct-hot-rolling study
- Temper
- not stated; do not infer O or an H temper
- Heat treatment
- base-comparison heat treatment is not stated
- Product form
- sheet
- Thickness / diameter range
- source feed sheet 6 mm; exact tensile-comparison specimen thickness not stated
- Test direction
- not stated
- Processing route
- commercial AA3105 sheet used to mill chips; base-comparison processing state is not explicit
- Temperature range
- Tensile-test temperature is not stated; no temperature extrapolation is allowed.
- Notes
- Measured comparison values for the exact AA3105 base material used in one recycling study. The source identifies the feed as 6 mm sheet but does not state temper, tensile direction, temperature or the base-comparison processing state precisely. These values are not EN product minima and do not describe the AA1050-enveloped recycled laminate.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI