Metal

EN AW-3103 thin-wall tube, 9.5 mm inside diameter x 12 mm outside diameter (1.25 mm nominal wall), tensile population (CC BY experimental)

Observed static-tensile averages and extremes for one exact EN AW-3103 thin-wall tube size.

Back Compare PDF data sheet
Properties
Mechanical
Property Value Unit
Young's modulus 65.132 GPa
Observed minimum young's modulus 38.375 GPa
Observed maximum young's modulus 67.575 GPa
Maximum tensile force Fm 5.0 kN
Observed minimum maximum tensile force fm 0.73 kN
Observed maximum maximum tensile force fm 5.21 kN
0.1% proof strength Rp0.1 99.0 MPa
Observed minimum 0.1% proof strength rp0.1 11.96 MPa
Observed maximum 0.1% proof strength rp0.1 104.66 MPa
Tensile yield strength 104.0 MPa
Observed minimum tensile yield strength 12.61 MPa
Observed maximum tensile yield strength 109.93 MPa
Ultimate tensile strength 114.0 MPa
Observed minimum ultimate tensile strength 17.02 MPa
Observed maximum ultimate tensile strength 121.31 MPa
Units
Condition
Condition
EN AW-3103 tube as tested; static-table temper and shaped/raw state not identified
Temper
not stated; do not infer O or an H temper
Heat treatment
not stated
Product form
extruded round thin-wall tube
Thickness / diameter range
9.5 mm inside diameter x 12 mm outside diameter (1.25 mm nominal wall)
Test direction
longitudinal tube tension
Processing route
commercial tube; manufacturing and any specimen shaping/tempering assignment are not stated for Table 1
Temperature range
The static tensile-test temperature is not reported.
Notes
Exact EN AW-3103 tube geometry and the article's static-tensile averages and observed extremes are retained. Temper, test temperature and exact per-size sample count are not stated, and the authors describe the results as inconsistent and sparse. The fatigue-stress ordinate was withheld under NDA and is not imported. Values are observations, not standard minima or design allowables.
Standards

No material standards linked.

Record status
Category
Metal
Unit system
Common SI