Composite
HexPly 913G-E-5-30 E-glass/913 UD layer inputs (CC BY)
Exact-product nominal cured-ply thickness and directional layer-model inputs for HexPly E-glass/913 UD prepreg.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 1900.0 | kg/m^3 |
| Ply thickness | 0.125 | mm |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Longitudinal tensile modulus | 38.7 | GPa |
| Transverse tensile modulus | 15.4 | GPa |
Units
Condition
- Condition
- HexPly 913G-E-5-30 E-glass/913 cured UD layer in an adaptive-inlet research panel
- Temper
- not applicable
- Heat treatment
- source panel vacuum-bag cured at 125 degC and 1 bar for 60 min with 2 degC/min heat-up
- Product form
- unidirectional E-glass/913 prepreg layer; three-to-six-ply variable-thickness panel
- Thickness / diameter range
- 0.125 mm nominal cured ply thickness
- Test direction
- longitudinal E1 and transverse E2 layer axes
- Processing route
- conventional UD prepreg, vacuum-bag cured for the reported research panel
- Temperature range
- Table 1 does not state a use or measurement temperature for the model inputs.
- Notes
- The article identifies the exact prepreg as conventional HexPly 913G-E-5-30 UD E-glass/913 and uses the Table 1 values as layer inputs for a research-panel finite-element model. It provides no batch identifier, material-test methods, sample counts, scatter, guarantee or qualification basis. The stated vacuum-bag cycle describes the demonstrated three-to-six-ply panel and is not represented as a universal supplier cure schedule. Table 1 prints Density 1900 without a unit; PropLib interprets the magnitude as kg/m^3, labels that interpretation explicitly and retains source_unit as not stated.
Standards
No material standards linked.
Record status
- Category
- Composite
- Unit system
- Common SI