AA6463 annealed properties (CC BY secondary reference)
Secondary tabulated mechanical-property row for exact AA6463 in annealed condition.
Properties
Mechanical
| Property | Value | Unit |
|---|---|---|
| Tensile yield strength | 50.0 | MPa |
| Ultimate tensile strength | 88.0 | MPa |
| Elongation | 23.0 | % |
| Shear strength | 70.0 | MPa |
| Fracture strength | 55.0 | MPa |
| Hardness (source heading H.V; printed unit HB) | 25.0 | HB (source-printed; heading conflict) |
Units
Condition
- Condition
- AA6463 annealed condition; the source does not print an O temper designation, secondary review table
- Temper
- annealed condition; the source does not print an O temper designation
- Heat treatment
- Table 9 lists AA6463 annealing temperature 413 degC; time, cooling route and the connection between the Table 9 process row and the Table 10 property population are not stated
- Product form
- not stated
- Thickness / diameter range
- not stated
- Test direction
- not stated
- Processing route
- wrought AA6XXX context; exact product route for the tabulated property row is not stated
- Temperature range
- The property table does not state test temperature; no temperature extrapolation is allowed.
- Notes
- Secondary values reproduced by a CC BY review from its reference [7]. The review gives no product form, size, direction, test temperature, test method, sample count, statistic or uncertainty for these property rows. The hardness heading is H.V while the printed unit row is HB, so PropLib preserves the inconsistency instead of choosing a hardness scale. These values are not current EN minima, supplier-certified values or design allowables.