Metal
AA3004 cast condition A3, compression reference (CC BY experimental)
Room- and elevated-temperature compression yield strength for laboratory AA3004 after 375 degC for 48 h.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Electrical conductivity | 37.8 | % IACS |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Compression yield strength at room temperature | 107.9 | MPa |
| Compression yield strength at 300 degC | 78.3 | MPa |
Units
Condition
- Condition
- laboratory permanent-mold cast AA3004, condition A3
- Temper
- experimental heat-treatment code A3; no registered temper claimed
- Heat treatment
- 375 degC for 48 h; direct water quench to room temperature
- Product form
- laboratory permanent-mold cast ingot; machined compression specimen
- Thickness / diameter range
- cast ingot 30 x 40 x 80 mm; specimen 10 mm diameter x 15 mm long
- Test direction
- compression direction not stated
- Processing route
- laboratory melt from commercial-purity feedstock, permanent-mold cast, heat treated and water quenched
- Temperature range
- 20 ... 300 degC
- Notes
- Experimental AA3004 compression data for one laboratory cast heat and condition A3; three-test mean and stated standard deviation. Not a wrought-product tensile minimum or EN temper.