Metal
AA5005-H32 rod, 10 mm (CC BY reference)
Reported mechanical and thermal base-material properties for exact AA5005-H32 used in a 10 mm rod.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2700.0 | kg/m^3 |
Thermal
| Property | Value | Unit |
|---|---|---|
| Thermal conductivity | 200.0 | W/m/K |
| Specific heat capacity | 900.0 | J/kg/K |
| Solidus temperature | 632.0 | degC |
| Liquidus temperature | 654.0 | degC |
| Linear thermal expansion coefficient | 2.19e-05 | 1/K |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Tensile yield strength | 117.0 | MPa |
| Ultimate tensile strength | 138.0 | MPa |
| Elongation | 11.0 | % |
| Young's modulus | 68.9 | GPa |
| Poisson's ratio | 0.33 | - |
| Shear modulus | 25.9 | GPa |
| Shear strength | 96.5 | MPa |
| Brinell hardness | 36.0 | HB |
Units
Condition
- Condition
- AA5005-H32 base material used as the aluminum rotating rod in a Ti Grade 2/AA5005 friction-welding study
- Temper
- H32
- Heat treatment
- strain hardened and stabilized to H32; detailed supplier route not stated
- Product form
- rod
- Thickness / diameter range
- 10 mm diameter; model component length 20 mm
- Test direction
- not stated for the reported reference values
- Processing route
- commercial H32 rod; detailed prior processing not stated
- Temperature range
- Mechanical-table temperature is not stated; thermal conductivity is marked as room-temperature.
- Notes
- Reported reference values for exact AA5005-H32 base material used in the article's 10 mm rod; source direction, sampling and value statistics are not stated. Values are not EN product minima.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI