Metal
AA5383 Mg5.0 wt.% Mg hot plane-strain compression matrix (CC BY experimental)
Measured composition, 200-500 degC peak-flow-stress matrix and Arrhenius activation energy for the Mg5.0-5383 experimental variant.
Properties
Mechanical
| Property | Value | Unit |
|---|---|---|
| Peak flow stress at 200 degC and 0.05 1/s | 338.16 | MPa |
| Peak flow stress at 260 degC and 0.05 1/s | 247.94 | MPa |
| Peak flow stress at 320 degC and 0.05 1/s | 183.37 | MPa |
| Peak flow stress at 380 degC and 0.05 1/s | 124.43 | MPa |
| Peak flow stress at 440 degC and 0.05 1/s | 73.78 | MPa |
| Peak flow stress at 500 degC and 0.05 1/s | 43.934 | MPa |
| Peak flow stress at 200 degC and 0.5 1/s | 352.17 | MPa |
| Peak flow stress at 260 degC and 0.5 1/s | 290.21 | MPa |
| Peak flow stress at 320 degC and 0.5 1/s | 221.31 | MPa |
| Peak flow stress at 380 degC and 0.5 1/s | 169.44 | MPa |
| Peak flow stress at 440 degC and 0.5 1/s | 118.8 | MPa |
| Peak flow stress at 500 degC and 0.5 1/s | 87.6 | MPa |
| Peak flow stress at 200 degC and 5 1/s | 348.57 | MPa |
| Peak flow stress at 260 degC and 5 1/s | 299.52 | MPa |
| Peak flow stress at 320 degC and 5 1/s | 241.77 | MPa |
| Peak flow stress at 380 degC and 5 1/s | 191.67 | MPa |
| Peak flow stress at 440 degC and 5 1/s | 150.54 | MPa |
| Peak flow stress at 500 degC and 5 1/s | 114.06 | MPa |
| Hot-deformation activation energy | 209.1821 | kJ/mol |
Composition
| Property | Value | Unit |
|---|---|---|
| Magnesium mass fraction | 5.03 | wt.% |
| Manganese mass fraction | 0.7 | wt.% |
| Silicon mass fraction | 0.09 | wt.% |
| Chromium mass fraction | 0.07 | wt.% |
| Iron mass fraction | 0.19 | wt.% |
Processing
| Property | Value | Unit |
|---|---|---|
| Peak power dissipation efficiency | 47.0 | % |
Units
Condition
- Condition
- experimental Mg5.0-5383 composition after the article's Gleeble thermal cycle and during plane-strain compression
- Temper
- initial temper not stated; do not infer H116
- Heat treatment
- 500 degC at 5 degC/s, 3 min hold, controlled cooling to test temperature, 2 min stabilisation; liquid-nitrogen quench after deformation
- Product form
- supplier 5383 alloy compressed in a Gleeble simulator; initial product form and specimen dimensions not stated in the article text
- Thickness / diameter range
- not reported
- Test direction
- plane-strain compression direction not stated
- Processing route
- hot plane-strain compression to 60 percent deformation; 1 degC/s cooling above 400 degC and 5 degC/s below 400 degC
- Temperature range
- 200 ... 500 degC
- Notes
- Exact article-designated Mg5.0-5383 chemistry and the full tabulated hot-compression matrix are retained. The article's reported full-strain safe region is 420-500 degC at 0.05-0.16 1/s over the article's full strain range. Initial temper, product form, specimen dimensions and replicate scatter are not stated. These peak flow stresses are not room-temperature tensile/yield values, standard minima or design allowables.