Metal
EN AW-5019 cold-worked H18 fine wire after 180 degC/3 h (CC BY experimental)
Single-wire tensile properties for exact EN AW-5019 supplied cold-worked H18 and then exposed at 180 degC for 3 h.
Properties
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength | 511.0 | MPa |
| Elastic limit strain | 0.62 | % |
| Failure strain | 0.81 | % |
Units
Condition
- Condition
- EN AW-5019 supplied cold-worked H18, after replacement heat treatment at 180 degC for 3 h
- Temper
- H18 before the replacement heat treatment
- Heat treatment
- replacement exposure at 180 degC for 3 h before single-wire testing
- Product form
- fine wire
- Thickness / diameter range
- 45 um diameter
- Test direction
- longitudinal wire direction
- Processing route
- commercial fine wire, replacement heat treatment, ASTM D3379-75 single-wire tension cardboard method
- Temperature range
- The single-wire test temperature is not reported.
- Notes
- Exact EN AW-5019 wire identity, as-supplied cold-worked H18 state and the subsequent 180 degC/3 h replacement thermal exposure are retained. Table 3 provides single tabulated results without replicate statistics or test temperature. The values are not delivery-state properties, generic temper values, product minima or design allowables. The paragraph identifies the cold-worked wire as H18 and 45 um diameter.