Metal
EN AW-5019 soft-annealed fine wire after 180 degC/3 h (CC BY experimental)
Single-wire tensile properties for exact EN AW-5019 supplied soft-annealed and then exposed at 180 degC for 3 h.
Properties
Mechanical
| Property | Value | Unit |
|---|---|---|
| Tensile yield strength | 164.0 | MPa |
| Ultimate tensile strength | 279.0 | MPa |
| Elastic limit strain | 0.19 | % |
| Failure strain | 8.92 | % |
Units
Condition
- Condition
- EN AW-5019 supplied soft-annealed, after replacement heat treatment at 180 degC for 3 h
- Temper
- soft-annealed supply state; no registered temper code stated
- Heat treatment
- replacement exposure at 180 degC for 3 h before single-wire testing
- Product form
- fine wire
- Thickness / diameter range
- Table 3 diameter not stated; do not infer 45 or 80 um
- Test direction
- longitudinal wire direction
- Processing route
- commercial fine wire, replacement heat treatment, ASTM D3379-75 single-wire tension cardboard method
- Temperature range
- The single-wire test temperature is not reported.
- Notes
- Exact EN AW-5019 wire identity, as-supplied soft-annealed state and the subsequent 180 degC/3 h replacement thermal exposure are retained. Table 3 provides single tabulated results without replicate statistics or test temperature. The values are not delivery-state properties, generic temper values, product minima or design allowables. The paragraph discusses more than one soft-annealed wire diameter and Table 3 does not explicitly bind its soft-annealed row to one diameter; no diameter is inferred.