EN AW-5251-H34 sheet, 1.2 mm, supplied state (CC BY experimental)
Five-test mean tensile strength, elongation and Vickers hardness plus measured chemistry for exact EN AW-5251-H34 sheet.
Properties
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength | 255.3 | MPa |
| Elongation A50 | 10.5 | % |
| Vickers hardness | 70.6 | HV0.3 |
Composition
| Property | Value | Unit |
|---|---|---|
| Magnesium mass fraction | 1.9 | % |
| Silicon mass fraction | 0.15 | % |
| Iron mass fraction | 0.4 | % |
| Manganese mass fraction | 0.5 | % |
| Copper mass fraction | 0.1 | % |
| Zinc mass fraction | 0.3 | % |
Units
Condition
- Condition
- EN AW-5251-H34 sheet in the supplied state before coating-removal thermal cycling
- Temper
- H34 (article describes the supplied state as one-half hard)
- Heat treatment
- as supplied H34; detailed prior strain-hardening/stabilization route not stated
- Product form
- sheet
- Thickness / diameter range
- 1.2 mm; test-program units 140 x 120 mm
- Test direction
- not stated for Table 2 tensile values
- Processing route
- commercial sheet supplied by CAMEBE; supply-state values retained before thermal cycles
- Temperature range
- Tensile- and hardness-test temperatures are not stated.
- Notes
- Experimental supply-state means for five tests on one 1.2 mm EN AW-5251-H34 sheet batch. Yield strength, tensile direction and test temperature are not reported. Thermal-cycle results are deliberately excluded. Not an EN minimum.