Metal
15-5PH H1025 plate, 4.75-25 mm (MIL-HDBK-5H)
Historical public-release S-basis reference for H1025 plate, conservatively combined across the applicable table bands.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 7833 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 1061.793 | MPa |
| Tensile yield strength, L | 985.95 | MPa |
| Ultimate tensile strength, LT | 1068.687 | MPa |
| Tensile yield strength, LT | 999.74 | MPa |
| Compressive yield strength, L | 1034.214 | MPa |
| Compressive yield strength, LT | 1027.319 | MPa |
| Ultimate shear strength | 668.791 | MPa |
| Elongation, LT | 8 | % |
| Young's modulus | 196.501 | GPa |
| Compression modulus | 201.327 | GPa |
| Shear modulus | 77.221 | GPa |
| Poisson's ratio | 0.27 | - |
Units
Condition
- Condition
- 15-5PH H1025; plate; 4.75-25.4 mm
- Temper
- H1025
- Heat treatment
- solution treated and aged to H1025; verify AMS 5862 schedule
- Product form
- plate
- Thickness / diameter range
- 0.187-1.000 in (4.75-25.4 mm)
- Test direction
- L and LT; the lower value across covered thickness bands is retained
- Processing route
- CEVM wrought precipitation-hardening stainless plate
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.