Metal
15-5PH H1150 bar/forging (MIL-HDBK-5H)
Historical public-release S-basis reference for 15-5PH H1150 bar and forging.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 7833 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 930.792 | MPa |
| Tensile yield strength, L | 723.95 | MPa |
| Ultimate tensile strength, LT | 930.792 | MPa |
| Tensile yield strength, LT | 723.95 | MPa |
| Compressive yield strength, L | 682.581 | MPa |
| Compressive yield strength, LT | 682.581 | MPa |
| Ultimate shear strength | 586.054 | MPa |
| Elongation, L | 16 | % |
| Elongation, LT | 11 | % |
| Ramberg-Osgood exponent, tension L | 9.0 | - |
| Young's modulus | 196.501 | GPa |
| Compression modulus | 201.327 | GPa |
| Shear modulus | 77.221 | GPa |
| Poisson's ratio | 0.27 | - |
Units
Condition
- Condition
- 15-5PH H1150; bar or forging; thickness/diameter <=304.8 mm
- Temper
- H1150
- Heat treatment
- solution treated and aged to H1150; verify AMS 5659 schedule
- Product form
- bar or forging
- Thickness / diameter range
- <=12 in (304.8 mm); includes the <=31 mm private-catalog scope
- Test direction
- L and transverse values as tabulated
- Processing route
- CEVM wrought precipitation-hardening stainless steel
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.