Metal
17-4PH H1025 bar (MIL-HDBK-5H)
Historical public-release S-basis reference for 17-4PH H1025 bar.
Properties
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 1068.687 | MPa |
| Tensile yield strength, L | 999.74 | MPa |
| Compressive yield strength, L | 958.371 | MPa |
| Ultimate shear strength | 655.002 | MPa |
| Elongation, L | 12 | % |
| Ramberg-Osgood exponent, tension L | 24 | - |
| Ramberg-Osgood exponent, compression L | 22 | - |
| Young's modulus | 196.501 | GPa |
| Compression modulus | 206.843 | GPa |
| Shear modulus | 77.221 | GPa |
| Poisson's ratio | 0.27 | - |
Units
Condition
- Condition
- 17-4PH H1025; bar; thickness/diameter <203.2 mm
- Temper
- H1025
- Heat treatment
- solution treated and aged to H1025; verify AMS 5643 schedule
- Product form
- bar
- Thickness / diameter range
- <8 in (203.2 mm); includes the <=114 mm private-catalog scope
- Test direction
- longitudinal
- Processing route
- wrought precipitation-hardening stainless bar
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI