Metal
Alclad 2024-T3 sheet, 1.6-6.3 mm (MIL-HDBK-5H)
Historical public-release 2024 alloy reference preserving T3 clad, clad flat sheet, material direction, and thickness scope.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2768 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 427.475 | MPa |
| Tensile yield strength, L | 310.264 | MPa |
| Ultimate tensile strength, LT | 420.58 | MPa |
| Tensile yield strength, LT | 275.79 | MPa |
| Compressive yield strength, L | 255.106 | MPa |
| Compressive yield strength, LT | 296.475 | MPa |
| Ultimate shear strength | 262.001 | MPa |
| Elongation, LT | 15 | % |
| Young's modulus | 72.395 | GPa |
| Compression modulus | 73.774 | GPa |
| Poisson's ratio | 0.33 | - |
| Shear modulus | 27.22 | GPa |
| Ramberg-Osgood exponent, tension L | 50 | - |
| Ramberg-Osgood exponent, tension LT | 15 | - |
| Ramberg-Osgood exponent, compression L | 13 | - |
| Ramberg-Osgood exponent, compression LT | 19 | - |
Units
Condition
- Condition
- 2024-T3 clad; clad flat sheet; 0.063-0.249 in (1.60-6.32 mm)
- Temper
- T3 clad
- Heat treatment
- 2024-T3 clad heat-treatment condition; verify the applicable procurement specification
- Product form
- clad flat sheet
- Thickness / diameter range
- 0.063-0.249 in (1.60-6.32 mm)
- Test direction
- L and LT material axes; lower tabulated values retained where bands are combined
- Processing route
- wrought heat-treatable aluminum alloy
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI