Metal
Aluminum 2024-T8510/T8511 extrusion, 6.35-38 mm (MIL-HDBK-5H)
Historical public-release S-basis T8510/T8511 extrusion reference through 38 mm quench thickness.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2768 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 455.054 | MPa |
| Tensile yield strength, L | 399.896 | MPa |
| Ultimate tensile strength, LT | 441.264 | MPa |
| Tensile yield strength, LT | 393.001 | MPa |
| Compressive yield strength, L | 406.791 | MPa |
| Compressive yield strength, LT | 406.791 | MPa |
| Ultimate shear strength | 248.211 | MPa |
| Elongation, LT | 5 | % |
| Ramberg-Osgood exponent, tension L | 24 | - |
| Ramberg-Osgood exponent, tension LT | 26 | - |
| Ramberg-Osgood exponent, compression L | 20 | - |
| Ramberg-Osgood exponent, compression LT | 24 | - |
| Young's modulus | 74.463 | GPa |
| Compression modulus | 75.842 | GPa |
| Shear modulus | 28.269 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 2024-T8510/T8511; extruded bar, rod or shape; 6.35-38 mm thickness at quench
- Temper
- T8510 or T8511
- Heat treatment
- solution heat treated, stress relieved by stretching and artificially aged
- Product form
- extruded bar, rod or shape
- Thickness / diameter range
- 0.250-1.496 in (6.35-38 mm), within the 0.250-1.499 in table column
- Test direction
- L and LT
- Processing route
- wrought heat-treatable aluminum extrusion
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI