Metal
Aluminum 2219-T62 sheet/plate, 3.2-50 mm (MIL-HDBK-5H)
Historical public-release heat-treatment-response reference for 2219-T62 sheet and plate.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2851 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 372.317 | MPa |
| Tensile yield strength, L | 248.211 | MPa |
| Ultimate tensile strength, LT | 372.317 | MPa |
| Tensile yield strength, LT | 248.211 | MPa |
| Compressive yield strength, L | 255.106 | MPa |
| Compressive yield strength, LT | 255.106 | MPa |
| Ultimate shear strength | 213.737 | MPa |
| Elongation, LT | 7 | % |
| Ramberg-Osgood exponent, tension L | 13 | - |
| Ramberg-Osgood exponent, tension LT | 13 | - |
| Ramberg-Osgood exponent, compression L | 16 | - |
| Ramberg-Osgood exponent, compression LT | 16 | - |
| Young's modulus | 72.395 | GPa |
| Compression modulus | 74.463 | GPa |
| Shear modulus | 27.579 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 2219-T62; sheet or plate; 3.2-50 mm
- Temper
- T62
- Heat treatment
- solution heat treated and artificially aged by the user; response-to-heat-treatment values
- Product form
- sheet or plate
- Thickness / diameter range
- 0.126-1.969 in (3.2-50 mm), within the 0.020-2.000 in table band
- Test direction
- L and LT
- Processing route
- wrought heat-treatable aluminum-copper sheet or plate
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.