Aluminum 2519-T87 plate, 25-50 mm (MIL-HDBK-5H)
Historical public-release S-basis weldable armor-plate reference; the handbook's labelled stress-strain page displays unrelated temperature-strength plots and is not numerically transcribed.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2823 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 455.054 | MPa |
| Tensile yield strength, L | 406.791 | MPa |
| Ultimate tensile strength, LT | 468.843 | MPa |
| Tensile yield strength, LT | 399.896 | MPa |
| Compressive yield strength, L | 393.001 | MPa |
| Compressive yield strength, LT | 413.685 | MPa |
| Ultimate shear strength | 282.685 | MPa |
| Elongation, L | 9 | % |
| Elongation, LT | 7 | % |
| Young's modulus | 72.395 | GPa |
| Compression modulus | 74.463 | GPa |
| Shear modulus | 27.579 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 2519-T87; plate; 25-50 mm
- Temper
- T87
- Heat treatment
- solution heat treated, cold worked and artificially aged
- Product form
- plate
- Thickness / diameter range
- 0.984-1.969 in (25-50 mm), within the 0.250-2.000 in table bands
- Test direction
- L and LT; lower listed value across applicable columns
- Processing route
- wrought weldable heat-treatable aluminum-copper plate
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI