Metal
Aluminum 5083-O sheet/plate, 1.3-6.3 mm (MIL-HDBK-5H)
Historical public-release A-basis annealed sheet/plate reference for the handbook's lower thickness band.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2657 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 275.79 | MPa |
| Tensile yield strength, L | 124.106 | MPa |
| Ultimate tensile strength, LT | 275.79 | MPa |
| Tensile yield strength, LT | 124.106 | MPa |
| Compressive yield strength, L | 124.106 | MPa |
| Compressive yield strength, LT | 124.106 | MPa |
| Ultimate shear strength | 172.369 | MPa |
| Elongation, L | 16 | % |
| Young's modulus | 70.327 | GPa |
| Compression modulus | 71.705 | GPa |
| Shear modulus | 26.545 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 5083-O; sheet or plate; 1.30-6.3 mm public counterpart range
- Temper
- O
- Heat treatment
- annealed
- Product form
- sheet or plate
- Thickness / diameter range
- 0.051-0.248 in (1.30-6.3 mm), subset of the 0.051-1.500 in table band
- Test direction
- L and LT
- Processing route
- wrought non-heat-treatable aluminum-magnesium sheet or plate
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI