Metal
Aluminum 6013-T6 sheet, 0.25-6.3 mm (MIL-HDBK-5H)
Historical public-release S-basis T6 sheet reference conservatively combined through 6.3 mm.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2713 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 358.527 | MPa |
| Tensile yield strength, L | 324.054 | MPa |
| Ultimate tensile strength, LT | 358.527 | MPa |
| Tensile yield strength, LT | 317.159 | MPa |
| Compressive yield strength, L | 330.948 | MPa |
| Compressive yield strength, LT | 330.948 | MPa |
| Ultimate shear strength | 220.632 | MPa |
| Elongation, LT | 8 | % |
| Young's modulus | 68.258 | GPa |
| Compression modulus | 69.637 | GPa |
| Shear modulus | 26.2 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 6013-T6; sheet; 0.25-6.3 mm
- Temper
- T6
- Heat treatment
- solution heat treated and artificially aged
- Product form
- sheet
- Thickness / diameter range
- 0.010-0.248 in (0.25-6.3 mm), within the 0.010-0.249 in table bands
- Test direction
- L and LT; lower listed value across size bands
- Processing route
- wrought heat-treatable aluminum sheet
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.