Aluminum 7010-T7451 plate, 12.7-38 mm (MIL-HDBK-5H)
Historical public-release 7010-T7451 plate reference.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2823 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 489.528 | MPa |
| Tensile yield strength, L | 427.475 | MPa |
| Ultimate tensile strength, LT | 496.423 | MPa |
| Tensile yield strength, LT | 427.475 | MPa |
| Compressive yield strength, L | 420.58 | MPa |
| Compressive yield strength, LT | 434.37 | MPa |
| Ultimate shear strength | 282.685 | MPa |
| Elongation, L | 9 | % |
| Elongation, LT | 6 | % |
| Ramberg-Osgood exponent, tension L | 12 | - |
| Ramberg-Osgood exponent, tension LT | 10 | - |
| Ramberg-Osgood exponent, compression L | 14 | - |
| Ramberg-Osgood exponent, compression LT | 17 | - |
| Young's modulus | 70.327 | GPa |
| Compression modulus | 73.084 | GPa |
| Shear modulus | 26.89 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 7010-T7451; plate; 12.7-38 mm
- Temper
- T7451
- Heat treatment
- solution heat treated, stress relieved by stretching and overaged to T74 condition
- Product form
- plate
- Thickness / diameter range
- 0.500-1.496 in (12.7-38 mm), within the 0.250-2.000 in table bands
- Test direction
- L and LT
- Processing route
- wrought heat-treatable aluminum-zinc plate
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.