Metal
Clad aluminum 7075-T6 sheet, 4.7-6.3 mm (MIL-HDBK-5H)
Historical public-release clad-sheet reference conservatively combined over 4.7-6.3 mm.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2796 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 503.317 | MPa |
| Tensile yield strength, L | 448.159 | MPa |
| Ultimate tensile strength, LT | 503.317 | MPa |
| Tensile yield strength, LT | 434.37 | MPa |
| Compressive yield strength, L | 441.264 | MPa |
| Compressive yield strength, LT | 461.949 | MPa |
| Ultimate shear strength | 303.369 | MPa |
| Elongation, LT | 8 | % |
| Ramberg-Osgood exponent, tension L | 17 | - |
| Ramberg-Osgood exponent, tension LT | 15 | - |
| Ramberg-Osgood exponent, compression L | 13 | - |
| Ramberg-Osgood exponent, compression LT | 12 | - |
| Young's modulus | 71.016 | GPa |
| Compression modulus | 72.395 | GPa |
| Poisson's ratio | 0.33 | - |
| Shear modulus | 26.7 | GPa |
Units
Condition
- Condition
- 7075-T6; clad sheet; 4.7-6.3 mm
- Temper
- T6 clad
- Heat treatment
- solution heat treated and artificially aged
- Product form
- clad sheet
- Thickness / diameter range
- 0.185-0.248 in (4.7-6.3 mm), within the 0.063-0.249 in table columns
- Test direction
- L and LT; lower listed value across applicable thickness columns
- Processing route
- clad wrought heat-treatable aluminum sheet
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI