Metal
Aluminum 7075-T62 extrusion, 6.35-38 mm (MIL-HDBK-5H)
Historical public-release response-heat-treated extrusion reference through 38 mm quench thickness.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2796 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 558.475 | MPa |
| Tensile yield strength, L | 496.423 | MPa |
| Ultimate tensile strength, LT | 517.107 | MPa |
| Tensile yield strength, LT | 448.159 | MPa |
| Compressive yield strength, L | 496.423 | MPa |
| Compressive yield strength, LT | 489.528 | MPa |
| Ultimate shear strength | 296.475 | MPa |
| Elongation, L | 7 | % |
| Ramberg-Osgood exponent, tension L | 33 | - |
| Ramberg-Osgood exponent, tension LT | 22 | - |
| Ramberg-Osgood exponent, compression L | 27 | - |
| Ramberg-Osgood exponent, compression LT | 23 | - |
| Young's modulus | 71.705 | GPa |
| Compression modulus | 73.774 | GPa |
| Shear modulus | 27.579 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 7075-T62; extrusion; 6.35-38 mm thickness at quench
- Temper
- T62
- Heat treatment
- solution heat treated and artificially aged by the user; observe the response-treatment table note
- Product form
- extruded rod, bar or shape
- Thickness / diameter range
- 0.250-1.496 in (6.35-38 mm), within the 0.250-1.499 in table columns
- Test direction
- L and LT; lower listed value across applicable thickness columns
- Processing route
- wrought heat-treatable aluminum extrusion
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI