Metal
Aluminum 7075-T62 plate, 6.35-50 mm (MIL-HDBK-5H)
Historical public-release A-basis response-heat-treated plate reference through 50 mm.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2796 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 503.317 | MPa |
| Tensile yield strength, L | 441.264 | MPa |
| Ultimate tensile strength, LT | 530.896 | MPa |
| Tensile yield strength, LT | 461.949 | MPa |
| Compressive yield strength, L | 468.843 | MPa |
| Compressive yield strength, LT | 468.843 | MPa |
| Ultimate shear strength | 296.475 | MPa |
| Elongation, LT | 6 | % |
| Ramberg-Osgood exponent, tension L | 22 | - |
| Ramberg-Osgood exponent, tension LT | 22 | - |
| Ramberg-Osgood exponent, compression L | 25 | - |
| Ramberg-Osgood exponent, compression LT | 22 | - |
| Young's modulus | 71.016 | GPa |
| Compression modulus | 73.084 | GPa |
| Shear modulus | 26.89 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 7075-T62; plate; 6.35-50 mm
- Temper
- T62
- Heat treatment
- solution heat treated and artificially aged by the user; observe the response-treatment table note
- Product form
- plate
- Thickness / diameter range
- 0.250-1.969 in (6.35-50 mm), within the 0.250-2.000 in table columns
- Test direction
- L and LT; lower listed value across applicable thickness columns
- Processing route
- wrought heat-treatable aluminum plate
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.