Metal
Aluminum 7475-T7351 plate, 12.7-100 mm (MIL-HDBK-5H)
Historical public-release 7475-T7351 plate reference through 100 mm.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2796 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 441.264 | MPa |
| Tensile yield strength, L | 358.527 | MPa |
| Ultimate tensile strength, LT | 441.264 | MPa |
| Tensile yield strength, LT | 358.527 | MPa |
| Compressive yield strength, L | 337.843 | MPa |
| Compressive yield strength, LT | 372.317 | MPa |
| Ultimate shear strength | 268.896 | MPa |
| Elongation, L | 9 | % |
| Elongation, LT | 7 | % |
| Ultimate tensile strength, ST | 434.37 | MPa |
| Tensile yield strength, ST | 344.738 | MPa |
| Compressive yield strength, ST | 372.317 | MPa |
| Elongation, ST | 3 | % |
| Ramberg-Osgood exponent, tension L | 15 | - |
| Ramberg-Osgood exponent, tension LT | 13 | - |
| Ramberg-Osgood exponent, tension ST | 13 | - |
| Ramberg-Osgood exponent, compression L | 20 | - |
| Ramberg-Osgood exponent, compression LT | 20 | - |
| Ramberg-Osgood exponent, compression ST | 19 | - |
| Young's modulus | 71.016 | GPa |
| Compression modulus | 73.084 | GPa |
| Shear modulus | 26.89 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 7475-T7351; plate; 12.7-100 mm
- Temper
- T7351
- Heat treatment
- solution heat treated, stress relieved by stretching and overaged to T73 condition
- Product form
- plate
- Thickness / diameter range
- 0.500-3.937 in (12.7-100 mm), within the 0.250-4.000 in table bands
- Test direction
- L, LT and ST; lower listed value across applicable columns
- Processing route
- wrought high-purity heat-treatable aluminum-zinc plate
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI