Metal
Inconel 625 annealed bar, 12.7-100 mm (MIL-HDBK-5H)
Historical public-release S-basis annealed-bar reference conservatively combined through 100 mm.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 8442 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 827.371 | MPa |
| Tensile yield strength, L | 413.685 | MPa |
| Compressive yield strength, L | 365.422 | MPa |
| Ultimate shear strength | 544.686 | MPa |
| Elongation, L | 30 | % |
| Ultimate tensile strength, ST | 813.581 | MPa |
| Tensile yield strength, ST | 393.001 | MPa |
| Compressive yield strength, ST | 413.685 | MPa |
| Young's modulus | 205.464 | GPa |
| Compression modulus | 205.464 | GPa |
| Shear modulus | 81.358 | GPa |
| Poisson's ratio | 0.28 | - |
Units
Condition
- Condition
- Inconel 625; annealed bar; 12.7-100 mm
- Temper
- annealed
- Heat treatment
- annealed at 1700-1900 degF for time commensurate with section per handbook section 6.3.3
- Product form
- bar
- Thickness / diameter range
- 0.500-3.937 in (12.7-100 mm), within the 0.500-3.999 in table bands
- Test direction
- L and ST where available; lower listed value across applicable size bands
- Processing route
- wrought solid-solution-strengthened nickel-alloy bar
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.