Inconel 706 AMS 5701 heat-treated bar, <50 mm (MIL-HDBK-5H)
Historical public-release S-basis bar reference for the AMS 5701 tensile heat treatment.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 8083 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 1172.109 | MPa |
| Tensile yield strength, L | 965.266 | MPa |
| Compressive yield strength, L | 1006.635 | MPa |
| Ultimate shear strength | 730.844 | MPa |
| Elongation, L | 12 | % |
| Young's modulus | 209.601 | GPa |
| Compression modulus | 209.601 | GPa |
| Shear modulus | 75.842 | GPa |
| Poisson's ratio | 0.38 | - |
Units
Condition
- Condition
- Inconel 706; heat treated per AMS 5701; bar; <50 mm public counterpart range
- Temper
- AMS 5701 tensile heat treatment
- Heat treatment
- 1800 degF solution treatment and precipitation treatment per the applicable AMS 5701 revision
- Product form
- bar
- Thickness / diameter range
- <1.969 in (50 mm), subset of the <2.500 in table column
- Test direction
- L
- Processing route
- vacuum-melted precipitation-hardened nickel-alloy bar
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.