Metal
Inconel 718 solution-treated-and-aged bar, 6.35-100 mm (MIL-HDBK-5H)
Historical public-release S-basis bar reference, conservatively combined across the applicable size bands.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 8221 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 1275.53 | MPa |
| Tensile yield strength, L | 1034.214 | MPa |
| Ultimate tensile strength, LT | 1241.056 | MPa |
| Tensile yield strength, LT | 1034.214 | MPa |
| Compressive yield strength, L | 1075.582 | MPa |
| Ultimate shear strength | 765.318 | MPa |
| Elongation, L | 12 | % |
| Elongation, LT | 6 | % |
Units
Condition
- Condition
- Inconel 718; solution treated and aged; bar; 6.35-100 mm
- Temper
- solution treated and aged
- Heat treatment
- solution treated and aged per AMS 5662/5663
- Product form
- bar
- Thickness / diameter range
- 0.250-3.937 in (6.35-100 mm), within the handbook's 0.250-4.000 in bands
- Test direction
- L and LT where listed; lower listed values retained across size bands
- Processing route
- wrought nickel-base superalloy bar
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.