Metal
Inconel 718 solution-treated-and-aged sheet, 0.25-6.3 mm (MIL-HDBK-5H)
Historical public-release sheet reference using the lower listed strength across the covered AMS 5596 thickness bands.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 8221 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 1241.056 | MPa |
| Tensile yield strength, L | 999.74 | MPa |
| Ultimate tensile strength, LT | 1241.056 | MPa |
| Tensile yield strength, LT | 1013.529 | MPa |
| Compressive yield strength, L | 1068.687 | MPa |
| Compressive yield strength, LT | 1089.372 | MPa |
| Ultimate shear strength | 854.95 | MPa |
| Elongation, LT | 12 | % |
| Young's modulus | 202.706 | GPa |
| Compression modulus | 213.048 | GPa |
| Shear modulus | 78.6 | GPa |
| Poisson's ratio | 0.29 | - |
Units
Condition
- Condition
- Inconel 718; solution treated and aged; AMS 5596 sheet; 0.25-6.32 mm
- Temper
- solution treated and aged
- Heat treatment
- solution treated and aged per AMS 5596
- Product form
- sheet
- Thickness / diameter range
- 0.010-0.249 in (0.25-6.32 mm)
- Test direction
- L and LT; lower listed values retained across thickness bands
- Processing route
- wrought nickel-base superalloy sheet
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI