Metal
Ti-13V-11Cr-3Al annealed sheet/plate, 0.305-6.3 mm (MIL-HDBK-5H)
Historical public-release S-basis annealed sheet/plate reference through 6.3 mm.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 4816 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 861.845 | MPa |
| Tensile yield strength, L | 827.371 | MPa |
| Ultimate tensile strength, LT | 861.845 | MPa |
| Tensile yield strength, LT | 827.371 | MPa |
| Elongation, L | 8 | % |
| Elongation, LT | 8 | % |
| Compressive yield strength, L | 827.371 | MPa |
| Compressive yield strength, LT | 827.371 | MPa |
| Ultimate shear strength | 634.318 | MPa |
| Young's modulus | 99.974 | GPa |
Units
Condition
- Condition
- Ti-13V-11Cr-3Al; annealed; sheet, strip or plate; 0.305-6.3 mm
- Temper
- annealed
- Heat treatment
- annealed per MIL-T-9046 Composition B-1
- Product form
- sheet, strip or plate
- Thickness / diameter range
- 0.012-0.248 in (0.305-6.3 mm), subset of the tabulated 0.012-4.000 in range
- Test direction
- L and LT; lower listed value across applicable thickness columns
- Processing route
- wrought beta titanium-alloy sheet or plate
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI