Metal
Ti-6Al-4V annealed extrusion, <=50.8 mm (MIL-HDBK-5H)
Historical public-release A-basis annealed-extrusion reference.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 4429 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 896.318 | MPa |
| Tensile yield strength, L | 827.371 | MPa |
| Ultimate tensile strength, LT | 896.318 | MPa |
| Tensile yield strength, LT | 827.371 | MPa |
| Compressive yield strength, L | 882.529 | MPa |
| Compressive yield strength, LT | 889.424 | MPa |
| Ultimate shear strength | 572.265 | MPa |
| Elongation, L | 10 | % |
| Elongation, LT | 8 | % |
| Young's modulus | 116.521 | GPa |
| Compression modulus | 118.59 | GPa |
| Shear modulus | 42.747 | GPa |
| Poisson's ratio | 0.31 | - |
Units
Condition
- Condition
- Ti-6Al-4V; annealed; extrusion; <=50.8 mm
- Temper
- annealed
- Heat treatment
- annealed per AMS 4935
- Product form
- extrusion
- Thickness / diameter range
- <=2.000 in (50.8 mm)
- Test direction
- L and LT, subject to the source-table transverse-dimension footnote
- Processing route
- wrought alpha-beta titanium-alloy extrusion
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI