Metal
A-286 solution-treated and aged sheet (NASA historical reference)
Historical design-reference mechanical properties for solution-treated-and-aged A-286 sheet, strip, and plate plus room-temperature density.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 7940 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength | 965.266 | MPa |
| Tensile yield strength | 655.002 | MPa |
| Ultimate shear strength | 627.423 | MPa |
| Elongation | 15 | % |
Units
Condition
- Condition
- A-286 solution treated and aged (STA) sheet, strip, or plate; historical design reference
- Temper
- STA
- Heat treatment
- solution treated and aged; verify the applicable schedule in the handbook and current specification
- Product form
- sheet, strip, and plate
- Thickness / diameter range
- greater than 0.004 in (0.102 mm)
- Test direction
- not stated in the cited table
- Processing route
- wrought precipitation-hardened iron-nickel-base alloy
- Temperature range
- 21 ... 21 degC
- Notes
- Historical reference data transcribed with the stated property semantics and SI conversions. Confirm against the official PDF, a current procurement specification, the actual product form and thickness, and a material test report before engineering use.