EN AW-6012 initial T3 tensile and hardness reference (CC BY experimental)
Room-temperature tensile, modulus and HV10 values for exact EN AW-6012 in the initial T3 state.
Properties
Mechanical
| Property | Value | Unit |
|---|---|---|
| Tensile yield strength | 309.0 | MPa |
| Ultimate tensile strength | 350.0 | MPa |
| Elongation | 17.0 | % |
| Reduction of area | 23.0 | % |
| Young's modulus | 75.0 | GPa |
| Vickers hardness HV10 | 103.0 | HV10 |
Chemical
| Property | Value | Unit |
|---|---|---|
| Silicon mass fraction | 1.13 | % |
| Iron mass fraction | 0.37 | % |
| Manganese mass fraction | 0.53 | % |
| Magnesium mass fraction | 0.83 | % |
| Chromium mass fraction | 0.2 | % |
| Bismuth mass fraction | 0.51 | % |
| Lead mass fraction | 0.83 | % |
Units
Condition
- Condition
- EN AW-6012 AlMgSiPb, initial T3
- Temper
- T3 as identified by the article
- Heat treatment
- solution annealed and naturally aged; exact T3 schedule not stated
- Product form
- source form not stated; machined round tensile specimen
- Thickness / diameter range
- 8 mm tensile-specimen diameter; remaining Figure 1 dimensions not numerically transcribed
- Test direction
- specimen long axis; relation to original processing direction not stated
- Processing route
- initial T3 material, machined round specimen, room-temperature tensile and cross-section hardness tests
- Temperature range
- 20 ... 20 degC
- Notes
- The article's exact T3 label, investigated-heat composition, six-measurement tensile means and ten-position hardness method are retained. Original stock form, processing direction, T3 schedule and dispersion are not stated. Values are experimental means, not standard minima or design allowables.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI