AA2011 wire rod, 6.00/6.35 mm, tensile and Voce calibration (CC BY experimental)
Measured composition, tensile response and fitted Voce hardening parameters for exact 2011 aluminium wire rods.
Properties
Mechanical
| Property | Value | Unit |
|---|---|---|
| Young's modulus | 68.2 | GPa |
| Tensile yield strength | 318.0 | MPa |
| Fracture strain | 24.8 | % |
| Voce hardening increment Q, uncoupled | 155.0 | MPa |
| Voce hardening rate b, uncoupled | 23.0 | - |
| Voce hardening increment Q, coupled | 170.5 | MPa |
| Voce hardening rate b, coupled | 23.4 | - |
Composition
| Property | Value | Unit |
|---|---|---|
| Aluminium mass fraction | 92.12 | wt.% |
| Copper mass fraction | 5.97 | wt.% |
| Silicon mass fraction | 0.36 | wt.% |
| Iron mass fraction | 0.52 | wt.% |
| Manganese mass fraction | 0.008 | wt.% |
| Magnesium mass fraction | 0.004 | wt.% |
| Chromium mass fraction | 0.004 | wt.% |
| Zinc mass fraction | 0.004 | wt.% |
| Titanium mass fraction | 0.008 | wt.% |
| Bismuth mass fraction | 0.49 | wt.% |
| Tin mass fraction | 0.004 | wt.% |
| Lead mass fraction | 0.49 | wt.% |
Units
Condition
- Condition
- 2011 aluminium wire rods as supplied for tensile and drawing experiments
- Temper
- not stated; do not infer T3 or T8
- Heat treatment
- not stated
- Product form
- wire rod
- Thickness / diameter range
- 6.00 and 6.35 mm initial diameters; 220 mm tensile-specimen length
- Test direction
- longitudinal wire direction
- Processing route
- commercial wire rods; prior processing history not stated
- Temperature range
- Tensile-test temperature is not reported.
- Notes
- Exact 2011 alloy identity, measured optical-emission composition, wire geometry, tensile method and fitted Voce semantics are retained. Temper, prior processing, test temperature and replicate statistics are not reported. No UTS or standard elongation is inferred; not a product minimum or design allowable.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI