AA5182 finally annealed sheet, 1 mm, 90 degree direction (CC BY experimental)
Measured room-temperature tensile properties with 95% confidence intervals for finally annealed AA5182 sheet tested at 90 degrees to the casting direction.
Properties
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, 90 deg | 260.0 | MPa |
| Tensile yield strength, 90 deg | 112.0 | MPa |
| Elongation, 90 deg | 25.0 | % |
Units
Condition
- Condition
- AA5182 sheet produced by industrial twin-roll continuous casting and thermomechanical rolling, finally annealed at 400 degC for 4 h
- Temper
- finally annealed experimental state; registered temper not stated
- Heat treatment
- homogenization at 500 degC for 8 h within the thermomechanical route; intermediate annealing before final thickness; final annealing at 400 degC for 4 h
- Product form
- sheet
- Thickness / diameter range
- 1 mm final thickness
- Test direction
- 90 deg relative to casting direction
- Processing route
- industrial twin-roll continuous casting at 6.91 mm, thermomechanical rolling with intermediate annealing, and final annealing
- Temperature range
- 20 ... 25 degC
- Notes
- Experimental averages and 95% confidence intervals for the study's AA5182 1 mm sheet tested at 90 degrees to the casting direction; the registered temper and sample count are not stated, and the values are not EN minima.