Metal
AA7005 hot-rolled plate, 3.3 mm, aged 120 degC for 192 h, RD (CC BY experimental)
Measured longitudinal tensile, conductivity and fatigue reference values for exact AA7005 hot-rolled plate after one fully stated solution-and-ageing schedule.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Electrical conductivity | 40.9 | % IACS |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Tensile yield strength, RD | 340.0 | MPa |
| Ultimate tensile strength, RD | 382.0 | MPa |
| Elongation, RD | 14.0 | % |
| Fatigue life at 185 MPa and R=0 | 942200.0 | cycles |
Units
Condition
- Condition
- commercial AA7005 hot-rolled plate, solution treated, water quenched and experimentally peak aged at 120 degC for 192 h
- Temper
- experimental peak-aged state; no registered T-temper suffix is claimed
- Heat treatment
- solution treatment at 470 degC for 90 min, water quench, no more than 10 min room-temperature rest, then artificial ageing at 120 degC for 192 h
- Product form
- hot-rolled plate
- Thickness / diameter range
- 3.3 mm
- Test direction
- longitudinal, loading parallel to rolling direction
- Processing route
- commercial hot-rolled plate supplied by Northeast Light Alloy Co., Ltd.
- Temperature range
- 25 ... 25 degC
- Notes
- Experimental values for one commercial AA7005 3.3 mm hot-rolled plate, one solution-and-ageing schedule and longitudinal direction. Five tensile and fatigue specimens were tested, but the cited text gives no dispersion. The state is not relabeled as a registered temper and the values are not EN product minima.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI