EN AW-1050A-H14 cold-rolled sheet, 0.8 mm (CC BY reference)
Manufacturer nominal strengths, reported constants and calibrated rolling-direction hardening parameters for exact EN AW-1050A-H14 sheet.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2700.0 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Tensile yield strength | 100.0 | MPa |
| Ultimate tensile strength | 116.0 | MPa |
| Calibrated initial yield stress, RD | 80.0 | MPa |
| Extended Voce saturation stress Q1, RD | 25.7 | MPa |
| Extended Voce rate parameter C1, RD | 1000.0 | - |
| Extended Voce saturation stress Q2, RD | 7.6 | MPa |
| Extended Voce rate parameter C2, RD | 21.4 | - |
| Young's modulus | 70.0 | GPa |
| Poisson's ratio | 0.3 | - |
| Shear modulus | 26.92 | GPa |
Composition
| Property | Value | Unit |
|---|---|---|
| Silicon mass fraction | 0.04 | % |
| Iron mass fraction | 0.32 | % |
| Copper mass fraction | 0.001 | % |
| Manganese mass fraction | 0.002 | % |
| Titanium mass fraction | 0.02 | % |
Units
Condition
- Condition
- EN AW-1050A-H14 low-strength, strain-hardened cold-rolled sheet supplied by Norsk Hydro ASA
- Temper
- H14
- Heat treatment
- H14 as supplied; detailed strain-hardening route is not stated
- Product form
- cold-rolled sheet
- Thickness / diameter range
- 0.8 mm
- Test direction
- nominal strengths are not direction-specific; hardening calibration uses one representative rolling-direction (0 deg) tensile test
- Processing route
- commercial cold-rolled plate/sheet; dog-bone coupons cut at 0, 45 and 90 deg
- Temperature range
- Tensile-test temperature is not stated; no temperature extrapolation is allowed.
- Notes
- Exact 0.8 mm EN AW-1050A-H14 sheet identity and nine-test campaign context are retained. The 100/116 MPa strengths are manufacturer nominal values, the Voce terms are calibrated to one representative RD curve, and Table 5 constants come from the article's prior source. No value is an EN minimum or design allowable.