EN AW-1200 rolled sheet, 0.8 mm, directional tensile reference (CC BY experimental)

Properties

Physical

Property	Value	Unit
Density	2701.657	kg/m^3

Mechanical

Property	Value	Unit
Young's modulus, RD	59.289	GPa
Tensile yield strength, RD	109.096	MPa
Ultimate tensile strength, RD	125.387	MPa
Elongation A80, RD	2.174	%
Young's modulus, DD	70.084	GPa
Tensile yield strength, DD	107.237	MPa
Ultimate tensile strength, DD	117.961	MPa
Elongation A80, DD	3.229	%
Young's modulus, TD	80.172	GPa
Tensile yield strength, TD	123.172	MPa
Ultimate tensile strength, TD	134.743	MPa
Elongation A80, TD	2.853	%
Young's modulus	69.848	GPa
Tensile yield strength	113.168	MPa
Ultimate tensile strength	126.03	MPa
Elongation A80	2.749	%

Composition

Property	Value	Unit
Minimum aluminum mass fraction	99.0	%
Maximum silicon plus iron mass fraction	0.6	%

Units

Condition

Condition: EN AW-1200 (Al 99.0) rolled sheet substrate used in a pre-painted-sheet forming study
Temper: not stated; do not infer O or an H temper
Heat treatment: substrate heat treatment is not stated
Product form: rolled sheet
Thickness / diameter range: 0.8 mm
Test direction: 0 deg (RD), 45 deg (DD) and 90 deg (TD) to rolling direction
Processing route: commercial rolled sheet; surface pretreatment/paint variants belong to later forming tests
Temperature range: 20 ... 20 degC
Notes: Exact EN AW-1200 rolled-sheet grade, 0.8 mm thickness, directions and 20 degC test temperature are retained. Temper, sample count and dispersion are not stated. Directional moduli show substantial spread and remain unaltered. These are one-study measurements, not EN minima.

Standards

No material standards linked.

Record status