Metal
17-4PH H900 bar (MIL-HDBK-5H)
Historical public-release A-basis reference for 17-4PH H900 bar.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 7806 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 1310.004 | MPa |
| Tensile yield strength, L | 1172.109 | MPa |
| Compressive yield strength, L | 1172.109 | MPa |
| Ultimate shear strength | 848.055 | MPa |
| Elongation, L | 10 | % |
| Ramberg-Osgood exponent, tension L | 11 | - |
| Young's modulus | 196.501 | GPa |
| Compression modulus | 206.843 | GPa |
| Shear modulus | 77.221 | GPa |
| Poisson's ratio | 0.27 | - |
Units
Condition
- Condition
- 17-4PH H900; bar; thickness/diameter <203.2 mm
- Temper
- H900
- Heat treatment
- solution treated and aged to H900; verify AMS 5643 schedule
- Product form
- bar
- Thickness / diameter range
- <8 in (203.2 mm); includes the <=114 mm private-catalog scope
- Test direction
- longitudinal
- Processing route
- wrought precipitation-hardening stainless bar
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI