Metal
Aluminum 2024-T3510/T3511 extrusion, 6.35-19 mm (MIL-HDBK-5H)
Historical public-release extrusion reference conservatively combined across 6.35-19 mm quench thickness.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2768 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 413.685 | MPa |
| Tensile yield strength, L | 303.369 | MPa |
| Ultimate tensile strength, LT | 372.317 | MPa |
| Tensile yield strength, LT | 255.106 | MPa |
| Compressive yield strength, L | 255.106 | MPa |
| Compressive yield strength, LT | 275.79 | MPa |
| Ultimate shear strength | 206.843 | MPa |
| Elongation, LT | 12 | % |
| Ramberg-Osgood exponent, tension L | 50 | - |
| Ramberg-Osgood exponent, tension LT | 14 | - |
| Ramberg-Osgood exponent, compression L | 16 | - |
| Ramberg-Osgood exponent, compression LT | 17 | - |
| Young's modulus | 74.463 | GPa |
| Compression modulus | 75.842 | GPa |
| Shear modulus | 28.269 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 2024-T3510/T3511; extruded bar, rod or shape; 6.35-19 mm thickness at quench
- Temper
- T3510 or T3511
- Heat treatment
- solution heat treated, stress relieved by stretching and naturally aged
- Product form
- extruded bar, rod or shape
- Thickness / diameter range
- 0.250-0.748 in (6.35-19 mm), within the 0.250-0.749 in table columns
- Test direction
- L and LT; lower listed value across applicable thickness columns
- Processing route
- wrought heat-treatable aluminum extrusion
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI