Metal
Aluminum 7075-T6/T651/T62 bar and rod, <=75 mm (MIL-HDBK-5H)
Historical public-release bar/rod reference conservatively combined through 75 mm.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2796 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 530.896 | MPa |
| Tensile yield strength, L | 455.054 | MPa |
| Ultimate tensile strength, LT | 496.423 | MPa |
| Tensile yield strength, LT | 434.37 | MPa |
| Compressive yield strength, L | 441.264 | MPa |
| Ultimate shear strength | 317.159 | MPa |
| Elongation, L | 7 | % |
| Ramberg-Osgood exponent, tension L | 50 | - |
| Ramberg-Osgood exponent, compression L | 13 | - |
| Young's modulus | 71.016 | GPa |
| Compression modulus | 72.395 | GPa |
| Shear modulus | 26.89 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 7075-T6/T651/T62; rolled, drawn or cold-finished bar/rod; <=75 mm
- Temper
- T6, T651 or T62
- Heat treatment
- solution heat treated and artificially aged; T62 denotes user response heat treatment
- Product form
- rolled, drawn or cold-finished bar or rod
- Thickness / diameter range
- <=2.953 in (75 mm), within the <=3.000 in table bands
- Test direction
- L and LT where available; lower listed value across applicable size bands
- Processing route
- wrought heat-treatable aluminum bar or rod
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI