Aluminum 7150-T7751 plate, 9-42.5 mm (MIL-HDBK-5H)
Historical public-release S-basis T7751 plate reference.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 2823 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 551.581 | MPa |
| Tensile yield strength, L | 510.212 | MPa |
| Ultimate tensile strength, LT | 551.581 | MPa |
| Tensile yield strength, LT | 510.212 | MPa |
| Compressive yield strength, L | 510.212 | MPa |
| Compressive yield strength, LT | 530.896 | MPa |
| Ultimate shear strength | 317.159 | MPa |
| Elongation, L | 7 | % |
| Elongation, LT | 6 | % |
| Ramberg-Osgood exponent, tension L | 12 | - |
| Ramberg-Osgood exponent, tension LT | 11 | - |
| Ramberg-Osgood exponent, compression L | 17 | - |
| Ramberg-Osgood exponent, compression LT | 22 | - |
| Young's modulus | 71.016 | GPa |
| Compression modulus | 73.774 | GPa |
| Shear modulus | 26.89 | GPa |
| Poisson's ratio | 0.33 | - |
Units
Condition
- Condition
- 7150-T7751; plate; 9-42.5 mm
- Temper
- T7751
- Heat treatment
- solution heat treated, stress relieved by stretching and overaged to T77 condition
- Product form
- plate
- Thickness / diameter range
- 0.354-1.673 in (9-42.5 mm), within the 0.250-3.000 in table bands
- Test direction
- L and LT; lower listed value across applicable columns
- Processing route
- wrought heat-treatable aluminum-zinc plate
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.