Metal
AISI 301 1/2 hard sheet/strip (MIL-HDBK-5H)
Historical public-release A-basis reference for cold-worked AISI 301 1/2 hard sheet and strip.
Properties
Physical
| Property | Value | Unit |
|---|---|---|
| Density | 7916 | kg/m^3 |
Mechanical
| Property | Value | Unit |
|---|---|---|
| Ultimate tensile strength, L | 972.161 | MPa |
| Tensile yield strength, L | 641.212 | MPa |
| Compressive yield strength, L | 420.58 | MPa |
| Ultimate shear strength | 530.896 | MPa |
| Elongation, LT | 15 | % |
| Young's modulus, L | 179.264 | GPa |
| Young's modulus | 193.053 | GPa |
| Compression modulus | 186.158 | GPa |
| Shear modulus | 72.395 | GPa |
| Poisson's ratio | 0.27 | - |
Units
Condition
- Condition
- AISI 301; 1/2 hard; sheet or strip
- Temper
- 1/2 hard
- Heat treatment
- cold worked to 1/2 hard condition
- Product form
- sheet or strip
- Thickness / diameter range
- strength table does not state a condition-specific bound; elongation covers <=0.015 and >=0.016 in bands where listed
- Test direction
- L strength; minimum elongation from the LT table
- Processing route
- cold-worked austenitic stainless sheet or strip
- Temperature range
- 21 ... 21 degC
- Notes
- Room-temperature historical handbook values. Applicability is limited to the exact alloy, temper/condition, product form, size band, material axis, statistical basis, and specification identified by the cited table. Historical reference only; confirm the current procurement specification and material test report.
Standards
No material standards linked.
Record status
- Category
- Metal
- Unit system
- Common SI